|本期目录/Table of Contents|

[1]何涛,詹有福,徐赫,等.催化剂铁中毒对催化裂化装置的影响及对策[J].石化技术与应用,2025,2:140-142.
　HE Tao,ZHAN You-fu,XU He,et al.Influence and countermeasures of iron poisoning of catalyst on fluid catalytic cracking unit[J].Petrochemical technology & application,2025,2:140-142.
点击复制

催化剂铁中毒对催化裂化装置的影响及对策(PDF)

《石化技术与应用》[ISSN:1009-0046/CN:62-1138/TQ]

期数:
2025年2期
页码:
140-142
栏目:
出版日期:
2025-03-10

文章信息/Info

Title:
Influence and countermeasures of iron poisoning of catalyst on fluid catalytic cracking unit
文章编号:
1009-0045（2025）02-0140-03
作者:
何涛1; 詹有福1; 徐赫1; 秦玉建1; 周梓桐1; 达伟1; 郑云锋2; 谭争国2
（1.中国石油云南石化有限公司 炼油一部，云南 安宁 650399；2.中国石油石油化工研究院 兰州化工研究中心，甘肃 兰州 730060）
Author(s):
HE Tao1; ZHAN You-fu1; XU He1; QIN Yu-jian1; ZHOU Zi-tong1; DA Wei1; ZHENG Yun-feng2;  TAN Zheng-guo2
（1.1st Department of Refining of Yunnan Petrochemical Company Co Ltd， PetroChina， Anning 650399， China；2.Lanzhou Petrochemical Research Center ， Petrochemical Research Institute， PetroChina， Lanzhou 730060， China）
关键词:
催化裂化; 催化剂; 铁中毒; 产品分布
Keywords:
fluid catalytic cracking;  catalyst;  iron poisoning;  product distribution
分类号:
TE 624.4+1
DOI:
DOI：10.19909/j.cnki.ISSN1009-0045.2025.02.0140
文献标识码:
B
摘要:
针对中国石油云南石化有限公司3.3 Mt/a催化裂化装置催化剂铁中毒的问题，对催化剂铁中毒原因及其对催化剂性质、装置操作工况及产品分布的影响进行了分析，并提出了相应的对策。结果表明：催化剂铁中毒后，其密度由0.93 g/mL降至0.82 g/mL，球形度变差；装置出现再生器藏量增加，烧焦罐藏量减少，油浆中固体质量浓度下降，产品分布变差等问题。通过采取优化再生器操作，置换平衡剂，补充新鲜催化剂，降低原料含铁量等措施，可缓解催化剂铁中毒对装置运行带来的影响，确保装置平稳高效运行。
Abstract:
In response to the problem of iron poisoning of catalyst in the 3.3 Mt/a fluid catalytic cracking unit of Yunnan Petrochemical Co Ltd，PetroChina， the causes of iron poisoning of catalyst and its influence on catalyst properties， unit operating conditions， and product distribution were analyzed， and corresponding countermeasures were proposed. The results showed that after iron poisoning of catalyst， its density decreased from 0.93 g/mL to 0.82 g/mL， and its sphericity deteriorated. The unit had problems such as increasing in the storage capacity of the regenerator， decreasing in the storage capacity of the coking tank， decreasing in the solid mass concentration in the oil slurry， and a deterioration in product distribution. By taking measures such as optimizing the operation of the regenerator， replacing the balancing agent， supplementing fresh catalyst， and reducing the iron content of the raw materials， the negative impact of iron poisoning catalyst on the operation of the unit could be alleviated， ensuring smooth and efficient operation of the unit.

参考文献/References

［1］ 许友好.我国催化裂化工艺技术进展［J］.中国科学，2014，44（1）：13-24.［2］ 白小春，刘锦芳，刘利忠，等.催化剂铁中毒对FCC装置的影响分析［J］.炼油与化工， 2018， 29（4）：17-19.［3］ 吕艳芬.铁对催化裂化催化剂的危害及其对策［J］.炼油设计，2002，32（3）：42-46.［4］ 焦峰，崔苗，张新华，等.催化裂化装置催化剂铁中毒原因分析及对策［J］.生产与应用，2020，23（4）：11-16.［5］ 王远，任金龙.催化裂化装置催化剂铁中毒原因分析与对策［J］.中国石油和化工标准与质量，2020（24）：104-106.［6］ 李宁，任飞，刘守军，等.CMT-1 HN催化剂在高含量铁污染条件下的工业应用［J］.石油炼制与化工，2019，50（2）：63-67.［7］ 李雪礼，段宏昌，谭争国，等.催化裂化催化剂铁中毒现象分析与解决方案［J］.化学工业与工程， 2021， 38（4）：37-43.［8］ 何晓京，王强.催化裂化装置催化剂铁中毒分析及应对措施［J］.安全、健康和环境， 2019， 19（11）：37-41.