Title:

Preparation and performance of selective hydrodesulfurization catalyst for needle coke raw material

文章编号:

1009-0045（2023）05-0332-04

作者:

甄涛; 宋君辉; 金吉海; 焦祖凯; 严金龙; 张铎

（中海油炼油化工科学研究院，北京 102200）

Author(s):

ZHEN Tao; SONG Jun-hui; JIN Ji-hai; JIAO Zu-kai; YAN Jin-long; ZHANG Duo

（Research Institute of Refining and Chemical Industry，CNOOC，Beijing 102200，China）

关键词:

络合浸渍; 碱性络合剂; 催化裂化油浆; 针状焦原料; 加氢脱硫; 催化剂

Keywords:

complexation impregnation; basic complexing agent; catalytic cracking slurry; needle coke raw material; hydrodesulfurization; catalyst

分类号:

TE 624.9+3

DOI:

DOI：10.19909/j.cnki.ISSN1009-0045.2023.05.0332

文献标识码:

B

摘要:

以改性氧化铝为载体，采用络合浸渍法，制备出低金属含量、高选择性脱硫催化剂。以催化裂化脱固油浆为原料，在反应温度为290~320 ℃，反应压力为6 MPa，氢油体积比为1 000∶1，体积空速为1.0 h-1的条件下，考察了所制备催化剂的选择性脱硫性能。结果表明：浸渍过程中添加酸性有机助剂，催化剂孔道拓宽，酸性增强，载体与活性金属相互作用增强；浸渍过程中添加碱性有机助剂，催化剂孔道拓宽，酸性降低，载体与活性金属相互作用减弱，有利于活性金属硫化形成更多活性位，催化剂的脱硫性能明显增强；在反应温度为320 ℃时，采用碱性络合剂制备的催化剂，加氢后产品含硫量降至4 970 μg/g，脱硫率为55.6%，3~4环芳烃质量分数为42.1%，保留率为83.9%，适合作为优质针状焦原料。

Abstract:

Using modified alumina as carrier, a high selective desulfurization catalyst with low metal content was prepared by complexation-impregnation method. The fluid catalytic cracking desolid slurry was used as raw material. The selective desulfurization performance of the catalyst was investigated at the reaction temperature of 290-320 ℃, the reaction pressure of 6 MPa, the hydrogen to oil volume ratio of 1 000∶1, and the space velocity of 1.0 h-1. The results showed that the addition of acidic organic additives during the impregnation process broadened the catalyst pores, enhanced acidity, and enhanced interaction between the carrier and the active metal. By adding alkaline organic additives, the catalyst pores were widened, the acidity was reduced, and the interaction between the carrier and the active metal was weakened. This was beneficial for the sulfurization of active metals to form more active sites, and the desulfurization performance of the catalyst was significantly enhanced. At the reaction temperature of 320 ℃, the catalyst prepared with basic complexing agent reduced the sulfur content of the product to 4 970 μg/g with the desulfurization rate of 55.6%. And the mass fraction of tricyclic and tetracyclic aromatic hydrocarbons had been reduced to 42.1% with the retention rate of 83.9%. This hydrogenation product was suitable as the high-quality needle coke raw material.

参考文献/References

［1］ 邓遵安,蔡国晏,李阳.高比例掺炼催化裂化油浆对延迟焦化装置的影响［J］.石油炼制与化工，2022，53（12）：8-12.［2］ 卢德庆，辛靖，朱元宝，等.流化催化裂化油浆综合利用的分析［J］.化工进展，2021，40（Z 1）：142-149.［3］ 程意茹，蒋定建，方晓玲，等.催化裂化油浆的应用研究［J］.中国石油和化工标准与质量，2016，36（15）：72-73.［4］ 张孔远，吴建民，李永浩，等.催化裂化油浆减压蒸馏制备针状焦原料的研究［J］.石油炼制与化工，2022，53（6）：93-97.［5］ 吴勇，丁巍，戴咏川，等.石油系针状焦生产原料的预处理工艺研究进展［J］.石油化工，2021，50（12）：1341-1348.［6］ 王新军，魏豪，焦建.中国针状焦市场发展现状及前景分析［J］.当代石油石化，2022，30（8）：16-21.［7］ 苏栋根.石油系针状焦的市场现状与生产技术难点［J］.石油化工技术与经济，2013，29（6）：23-26.［8］ 蔡闯，代玉亭，王兵，等.国产针状焦技术瓶颈及突破［J］.燃料与化工，2021，52（3）：6-7.［9］ 潘会会. 纳米催化剂的制备及其对催化油浆的加氢行为研究［D］.青岛：中国石油大学（华东），2020.［10］ 李海栋. 催化裂化油浆“分子组谱”及加氢脱硫过程分子转化［D］.北京：中国石油大学（北京），2019.

备注/Memo

备注/Memo:

中海石油炼化有限公司资助项目（项目编号：LHTISA 20210044）

常用功能

更新日期/Last Update: 2023-09-10