Title:
Properties comparison of chromium-based small hollow special high density polyethylene series resins
文章编号:
1009-0045（2025）01-0017-05
作者:
邸麟婷; 杨世元; 秦晨元; 王文英; 魏福庆; 许惠芳
（中国石油石油化工研究院 兰州化工研究中心，甘肃 兰州 730060）
Author(s):
DI Lin-ting; YANG Shi-yuan; QIN Chen-yuan; WANG Wen-ying; WEI Fu-qing; XU Hui-fang（Lanzhou Petrochemical Research Center; Petrochemical Research Institute; PetroChina; Lanzhou 730060; China）
（Lanzhou Petrochemical Research Center，Petrochemical Research Institute，PetroChina，Lanzhou 730060，China）
关键词:
高密度聚乙烯; 淤浆法; 环管工艺; 铬系催化剂; 分子结构; 流变性能; 熔体强度
Keywords:
high density polyethylene; the slurry method; ring pipe process; chromium catalyst; molecular structure; rheological property; melt strength
分类号:
TQ 325.1
DOI:
DOI：10.19909/j.cnki.ISSN1009-0045.2025.01.0017
文献标识码:
B
摘要:
利用万能试验机、熔体流动速率仪、差示扫描量热仪、高温凝胶色谱仪和高压毛细管流变仪等仪器，对4家不同企业基于淤浆法环管工艺铬系催化剂条件下生产的小中空高密度聚乙烯（HDPE）树脂进行了表征和性能分析，并揭示了树脂结构对加工性能的影响。结果表明：这4种HDPE树脂在熔体流动速率、密度、拉伸性能等基础性能指标上存在一定范围的变化，体现了不同生产条件下树脂结构的多样性；辽宁华锦化工集团有限公司（简称华锦）和陕西延长石油延安能源化工有限责任公司（简称延能化）5502 S的相对分子质量较高，表明其拉伸模量较大，从而影响材料的耐用性和加工性能；热性能分析进一步表明，华锦5502 S具有较高的熔融温度，分子链规整性较好；浙江石油化工有限公司5502 S则表现出较高的结晶温度，能够在较高温度下实现快速结晶；华锦5502 S和延能化5502 S在低剪切速率下黏度较高，随着剪切速率的增加黏度迅速下降，而中国石油独山子石化公司5502 XA则表现出剪切变稠的特征。此外，华锦5502 S在高剪切速率下的弹性恢复力优异，进一步增强了其挤出胀大比。
Abstract:
The characterization and performance analysis of small hollow high density polyethylene （HDPE） resins produced by four different enterprises based on slurry ring pipe process of chromium-based catalyst were carried out by using universal testing machine, melt flow rate meter, differential scanning calorimeter, high temperature gel chromatograph and high pressure capillary rheometer, and the influence of resin structure on processing performance was revealed. The results showed that the four kinds of HDPE resins had a certain range of changes in the basic performance indexes such as melt flow rate, density and tensile properties, which reflected the diversity of resin structure under different production conditions. The relative molecular mass of 5502 S from Liaoning Huajin Chemical Group Co Ltd （hereinafter referred to as Huajin） and Shaanxi Yanchang Petroleum Yan′an Energy and Chemical Co Ltd （hereinafter referred to as Yannenghua） was relatively high, indicating that its tensile modulus was large, which affected the durability and processing performance of the material. The thermal performance analysis further showed that Huajin 5502 S had higher melting temperature and better molecular chain regularity. Zhejiang Petrochemical Co Ltd 5502 S showed a higher crystallization temperature and could achieve rapid crystallization at higher temperatures. Huajin 5502 S and Yannenghua 5502 S had high viscosity at low shear rate, and the viscosity decreased rapidly with the increase of shear rate, while Dushanzi Petrochemical Company of PetroChina 5502 XA showed the characteristics of shear thickening. In addition, Huajin 5502 S had excellent elastic resilience at high shear rate, which further enhanced the extrusion swell ratio.

参考文献/References

［1］ 王喆，侯昊飞，刘涛.三釜串联淤浆法制备的管材专用耐热聚乙烯的稳定性［J］.合成树脂及塑料，2022，37（1）：64-66.［2］ 王安晨，郭云亮，刘志远，等.国内淤浆法聚乙烯的工艺概况［J］.弹性体，2021，31（5）：84-88.［3］ 张昊霖.系统划分方法在淤浆法高密度聚乙烯工艺中的应用［J］.信息记录材料，2022，23（7）：64-67.［4］ 邓东升.Hostalen淤浆法高密度聚乙烯工艺副产物蜡的排出操作及技术改造［J］.化工技术与开发，2021，50（6）：64-65.［5］ 郭云亮，池亮，刘爱民，等.降低Hostalen低压淤浆工艺聚乙烯装置协议品量的方法［J］.化工科技，2022，30（3）：39-42.［6］ 李泽博，曹云峰，王鹏，等.Hostalen工艺淤浆法高密度聚乙烯装置己烷精制系统堵塞原因分析［J］.石油化工，2021，50（8）：802-807.［7］ 赵立超，张敏锋，王维.BCE-H 100催化剂在Hostalen工艺装置生产注塑料［J］.化工设计通讯，2018，44（1）：74.［8］ 马宝军.Hostalen工艺HDPE装置催化剂活性低的影响因素［J］.合成树脂及塑料，2021，38（5）：48-51.［9］ 张永涛，张威.双峰HDPE小中空容器专用树脂的结构与性能［J］.现代塑料加工应用，2019，31（4）：36-38.［10］ 王品凹，王华.不同生产工艺的小中空专用树脂的性能及应用［J］.化学与粘合，2019，41（1）：76-78.［11］ 翟昌休，高宇新，赵兴龙.Philips环管淤浆法聚乙烯生产工艺及其催化剂研究进展［J］.精细石油化工进展，2021，22（4）：44-49.［12］ 崔侨.国外高密度聚乙烯生产工艺对比［J］.石化技术，2023，30（7）：251-253.［13］ 丁书兵，李天朝，胡智超.高密度聚乙烯原料预处理工艺流程优化与研究［J］.石化技术，2022，29（6）：4-6.［14］ 吉豪杰，王高生，杨帆，等.聚乙烯大中空吹塑专用树脂的开发与性能研究［J］.当代化工，2022，51（5）：1049-1052.［15］ 张鹏，朱珍珍，朱裕国，等.高密度聚乙烯的结构与性能分析［J］.化工技术与开发，2021，50（9）：31-33.［16］ 王君豪，黄萍，单秀，等.HDPE和HDPE/SBR TPV非等温结晶行为的研究［J］.特种橡胶制品，2023，44（1）：39-44.［17］ 邹思敏，江太君，胡灿，等.熔融高密度聚乙烯的剪切黏度研究［J］.化工技术与开发，2020，49（2/3）：10-12.［18］ 董春钢，张海峰，马梦绮，等.弹性体模量对聚乙烯共混物结构与性能的影响［J］.当代化工，2022，51（5）：1093-1097.