[1]安彦杰,姜艳峰,李瑞,等.线性低密度聚乙烯人造草丝专用料制备与表征[J].石化技术与应用,2023,5:340-344.
　AN Yan-jie,JIANG Yan-feng,LI Rui,et al.Preparation and characterization of artificial grass silk special material for linear low density polyethylene[J].Petrochemical technology & application,2023,5:340-344.
点击复制

线性低密度聚乙烯人造草丝专用料制备与表征(PDF)

《石化技术与应用》[ISSN:1009-0046/CN:62-1138/TQ]

期数:
2023年5期
页码:
340-344
栏目:
出版日期:
2023-09-10

文章信息/Info

Title:
Preparation and characterization of artificial grass silk special material for linear low density polyethylene
文章编号:
1009-0045（2023）05-0340-05
作者:
安彦杰1; 姜艳峰1; 李瑞1; 吴双1; 姜泽钰1; 王宇1; 刘海峰2
（1.中国石油石油化工研究院 大庆化工研究中心，黑龙江 大庆 163714；2.大庆中蓝石化有限公司，黑龙江 大庆 163714）
Author(s):
AN Yan-jie1; JIANG Yan-feng1; LI Rui1; WU Shuang1; JIANG Ze-yu1; WANG Yu1; LIU Hai-feng2
（1. Daqing Petrochemical Research Center，Petrochemical Research Institute，PetroChina，Daqing 163714，China；2.Daqing Zhonglan Petrochemical Co Ltd，Daqing 163714，China）
关键词:
人造草丝; 线性低密度聚乙烯; 熔体流动速率; 耐磨转数; 运动草坪
Keywords:
artificial grass silk; linear low density polyethylene; melt flow rate; wear-resisting rotation; sports lawn
分类号:
TQ 325.1+2
DOI:
DOI：10.19909/j.cnki.ISSN1009-0045.2023.05.0340
文献标识码:
B
摘要:
在50 kg/h气相法聚乙烯中试装置上进行了线性低密度聚乙烯草丝专用料的生产，并开展了加工应用试验。结果表明：所生产草丝专用料的熔体流动速率为0.22 g/min，密度为0.926 g/cm3，各项性能达到指标设计要求；制备的人造草丝的耐磨转数达到25 000转，断裂平均力为26.5 N，断裂伸长率为48%，达到运动草坪的性能指标要求。
Abstract:
The production of the grass silk special material for linear low density polyethylene was carried out on the 50 kg/h gas phase polyethylene pilot plant, and the processing and application test was completed. The results showed that the melt flow rate and density of the grass silk special material were 0.22 g/min and 0.926 g/cm3, and the performance met the design requirements. The wear-resisting rotation of the artificial grass silk was 25 000 r； the average breaking force was 26.5 N； and the elongation at break was 48%. All the properties of the artificial grass silk reached the index requirements of sports lawn.

参考文献/References

［1］ 高炜斌，王自瑛，薛叙明. 低温固化人造草坪用背胶的性能研究［J］. 中国胶黏剂，2016，25（12）:14-17.［2］ 赵紫昱，马丕波. 人造草坪的发展现状［J］. 纺织科技进展, 2019（4）:8-11.［3］ 陈燕，袁爽，冯志新，等. 聚烯烃人造草坪丝耐候性能的研究［J］. 合成材料老化与应用，2018，47（6）:10-12.［4］ Calloway S P，Hardin D M，Crawford M D，et al. Injury surveillance in major league soccer: A 4-year comparison of injury on natural grass versus artificial turf field［J］. The American Journal of Sports Medicine, 2019, 47（10）:2279-2286.［5］ Mohajerani A，Kurmus H，Tran L，et al．Clegg impact hammer： An equipment for evaluation of the strength characteristics of pavement materials，turf，and natural and artificial playing surfaces：A review［J］．Road Materials and Pavement Design, 2020, 21（2）:467-485. ［6］ 赵静岚，林珩，郑柏存. 回收料制备人造草丝熔体的流变性能研究［J］. 塑料工业， 2010，38（1）:66-69.［7］ 魏婷，公维光，郑柏存. 草香型人造运动草丝的研制与释香性能研究［J］. 塑料工业， 2008，36（8）:57-59.［8］ 徐捷. 草制品和草坪染色［J］. 染料与染色，2011，48（4）:30-35.［9］ 芦长椿. 人造草坪的技术发展及应用［J］. 纺织导报， 2011（6）:63-65.［10］ Luijkx R，喻盈捷，林夕.合成草坪纱用Lumicene茂金属聚乙烯［J］.国际纺织导报，2010（11）:11-12.［11］ 王伟山，郑柏存，易红玲. 纳米碳酸钙在运动草坪纤维中的应用研究［J］. 工程塑料应用，2008，36（8）:56-59.［12］ 林珩，傅乐峰，郑柏存. 人造草坪的测试标准与FIFA品质概念［J］．中国体育运动材料与装备，2007，11（1）:17-19. ［13］ Yi H，Zheng B，Lin H，et al. Nanosilica and polyethylene based artificial turf-abrasion resistance and mechanical properties［J］. Procedia Engineering，2014，72:901-906.