Title:

Performance of Ag modified HZSM-5 catalyst for isomerization of1，2，4-trimethylbenzene to 1，3，5-trimethylbenzene

文章编号:

1009-0045（2023）06-0433-04

作者:

王福善1; 杨俊明1; 张霖1; 张昊2; 3; 梁琨2; 3*

1.中国石油兰州石化公司，甘肃 兰州 730060；2.兰州大学 化学化工学院，甘肃 兰州 730000；3.有色金属催化剂国家地方联合工程实验室，甘肃 兰州 730000

Author(s):

WANG Fu-shan1; YANG Jun-ming1; ZHANG Lin1; ZHANG Hao2; 3; LIANG Kun2; 3

1.Lanzhou Petrochemical Company，PetroChina，Lanzhou 730060，China；2.College of Chemistry and Chemical Engineering，Lanzhou University，Lanzhou 730000，China；3.National and Local Joint Engineering Laboratory of Nonferrous Metal Chemical Catalysts，Lanzhou 730000，China

关键词:

HZSM-5催化剂; 异构化; Ag改性; 偏三甲苯; 均三甲苯; 转化率; 选择性; 收率

Keywords:

HZSM-5 catalyst; isomerization; Ag modification; 1; 2; 4-trimethylbenzene; 1; 3; 5-trimethylbenzene; conversion rate; selectivity; yield

分类号:

TQ 426.99；TQ 241

DOI:

DOI：10.19909/j.cnki.ISSN1009-0045.2023.06.0433

文献标识码:

B

摘要:

在偏三甲苯异构化制均三甲苯反应中，以理想三甲苯混合系统为模型，通过热力学计算，得到混合三甲苯体系在不同反应温度下的平衡组成，以及偏三甲苯异构化反应温度区间内偏三甲苯转化率、均三甲苯选择性及其收率；在此基础上，对HZSM-5催化剂进行Ag金属改性，在加压固定床上评价其对偏三甲苯异构化的催化性能，并对反应温度、反应压力、质量空速等工艺条件进行优化。结果表明：在混合三甲苯的平均热力学平衡组成中，n（连三甲苯）∶n（偏三甲苯）∶n（均三甲苯）为0.052∶0.674∶0.274；在异构化反应温度区间内，偏三甲苯的转化率为32.6%，均三甲苯的选择性、收率分别为75.6%，27.4%；在反应温度280 ℃、反应压力1.6 MPa、质量空速1.0 h-1、Ag加入质量分数1%、氢油摩尔比为5的优化反应条件下，偏三甲苯的转化率为33.80%，均三甲苯的选择性为71.34%，均三甲苯单程收率最高可达24.90%。

Abstract:

Using an ideal trimethylbenzene mixture system as a model in the isomerization of 1，2，4-trimethylbenzene to 1，3，5-trimethylbenzene，the thermodynamic equilibrium composition of mixed trimethylbenzene at different temperatures and the conversion rate of 1，2，4-trimethylbenzene，the selectivity and yield of 1，3，5-trimethylbenzene within the reaction temperature range were obtained through the thermodynamic calculations. The isomerization reaction was carried out by HZSM-5 catalyst modified with Ag and its performance for the isomerization was evaluated in a pressurized fixed bed reactor. The process conditions of reaction temperature，reaction pressure，mass space velocity，and Ag addition mass fraction were optimized. The results showed that n（1，2，3-trimethylbenzene）∶n（1，2，4-trimethylbenzene）∶n（1，3，5-trimethylbenzene） was 0.052∶0.674∶0.274 in the average thermodynamic equilibrium composition of mixed trimethylbenzene. The conversion rate of 1，2，4-trimethylbenzene was 32.6%，the selectivity and yield of 1，3，5-trimethylbenzene were 75.6% and 27.4% respectively within the reaction temperature range. The conversion rate of 1，2，4-trimethylbenzene was 33.80%，and the selectivity of 1，3，5-trimethylbenzene was 71.34%，and the highest one-way yield of 1，3，5-trimethylbenzene could reach 24.90% under the optimized conditions of the reaction temperature at 280 ℃，the reaction pressure at 1.6 MPa，and the mass space velocity at 1.0 h-1，Ag addition mass fraction at 1%，and the molar ratio of hydrogen to oil at 5.

参考文献/References

［1］ Tsoung Y Y. Pseudocumene and mesitylene production and coproduction thereof with xylene：US，5004854［P］. 1991-04-02.［2］ Schutz A A ，Cullo L A. Method of making mesitylene：US，5087781［P］. 1992-02-11.［3］ Berg L. Separation of mesitylene from 1，2，4-trimethyl-benzene by azeotropic distillation：US，6136155［P］. 2000-10-24.［4］ Dalloro L，Cesana A，Buzzoni R，et al. Process for the production of mesitylene：US，20040225170［P］. 2004-11-17.［5］ Dalloro L，Cesana A，Buzzoni R，et al. Process for the production of mesitylene and durene：US，6949687［P］. 2005-05-18.［6］ Dalloro L，Cesana A，Buzzoni R，et al. Process for the production of mesitylene：US，7157397［P］. 2007-01-02.［7］ 王明. 偏三甲苯异构化制取均三甲苯研究［D］. 天津：天津大学，2014.［8］ 王燕，王明，张旭斌，等. Ni-Mo/HM上偏三甲苯异构化性能研究［J］.化学工业与工程，2016，33（1）：35-39.［9］ 张卫江，曲红梅，孙兴华，等. 1，3，5-三甲苯联产1，2，4，5-四甲苯生产工艺的研究［J］.天津大学学报，2002，35（1）：108-112.［10］ 周婷，陈晓蓉，陈长林. 改性WO3/ZrO2催化剂上偏三甲苯异构化［J］.南京工业大学学报（自然科学版），2008，30（3）：21-25.［11］ John A D. Lange′s Handbook of Chemistry［M］. United States of America：McGraw-Hill Book Company，1967：962-963.