Title:

Research progress on hydrotalcite-derived composite oxide as selective catalytic reduction denitrification catalyst

文章编号:

1009-0045（2023）06-0491-05

作者:

王玉斌1; 蒲欣1; 沈聪1; 刘军强1; 李勃呈2; 王远2

1.中国石油石油化工研究院 兰州化工研究中心，甘肃 兰州 730060；2.中国石油辽阳石化公司 油化运行部，辽宁 辽阳 111003

Author(s):

WANG Yu-bin1; PU Xin; SHEN Cong1; LIU Jun-qiang1; LI Bo-cheng2; WANG Yuan2

1. Lanzhou Petrochemical Research Center，Petrochemical Research Institute，PetroChina，Lanzhou 730060，China；2. Oil Chemical Operations Department of Liaoyang Petrochemical Company，PetroChina，Liaoyang 111003，China

关键词:

复合金属氧化物; 类水滑石（LDHs）; 类水滑石衍生复合氧化物（LDO）; 选择性催化还原; 氮氧化物（NOx）; 脱硝催化剂; 活性温度; 抗水抗硫性能

Keywords:

composite metal oxide; hydrotalcite-likes （LDHs）; hydrotalcite-like composite oxidized derivatives（LDO）; selective catalytic reduction; nitrogen oxides（NOx）; denitration catalyst; activation temperature; water and sulfur resistance

分类号:

TQ 426.83

DOI:

DOI：10.19909/j.cnki.ISSN1009-0045.2023.06.0491

文献标识码:

A

摘要:

综述了Cu 系、Mn 系等类水滑石衍生复合氧化物（LDO）用作选择性催化还原（SCR）脱硝催化剂的研究进展，重点分析了制备方法、金属改性、载体种类等对此类LDO催化剂脱硝效率、活性温度及抗水抗硫性能的影响。指出今后此类LDO催化剂的研发方向是：（1）采用包覆、掺杂等方式改善催化剂抗水抗硫性能；（2）利用涂覆、一体挤出等方式制备适用于较大处理量的成型催化剂。

Abstract:

The research progress on selective catalytic reduction （SCR） denitrification catalysts deriving from Cu，Mn and other based hydrotalcite-like composite oxides（LDO）was reviewed. And the effects of preparation methods，metal modifications，and carrier types on the denitrification efficiency，activation temperature and water and sulfur resistance of such catalysts were emphatically analyzed. Finally，it was pointed out that the future research & development directions of such LDO catalysts were：（1） to improve the water and sulfur resistance of the catalysts by cladding，doping，and other methods；（2） to prepare the molding catalysts suitable for large handling capacity via using the methods such as coating and integrated extrusion.

参考文献/References

［1］ 中华人民共和国生态环境部. 2021年中国生态环境统计年报［R］. 北京：中华人民共和国生态环境部，2023：19-20.［2］ 熊蔚立，黄伟，张国斌. 火电厂氮氧化物（NOx）的危害和防治［J］. 湖南电力，2002，22（1）：61-62.［3］ 苏涛. 大气中氮氧化物的形成及防治［J］. 科学咨询，2009（6）：43-44.［4］ 刘军强，贾媛媛，张鹏，等. 分子筛NH3-SCR脱硝催化剂研究进展［J］. 石油化工，2020，49（10）：1012-1021.［5］ 杨玲，李茂，李建军. SCR催化剂的研究进展［J］. 四川化工，2012，15（6）：26-29.［6］ Li J H，Chang H Z，Ma L，et al. Low-temperature selective catalytic reduction of NOx with NH3 over metal oxide and zeolite catalysts-A review［J］. Catalysis Today，2011，175（1）：147-156.［7］ Nova I，Dall A L，Lietti L，et al. Study of thermal deactivation of a de-NOx commercial catalyst［J］. Applied Catalysis B（Environmental），2001，35（1）：31-42.［8］ 王岚，詹正坤. 水滑石类阴离子黏土的合成及催化应用研究进展［J］. 化学研究与应用，2003，15（4）：437-442.［9］ 王玉斌，陈彤，王公应. 固体碱KF/MgAl-LDO催化苯酚与碳酸二甲酯合成苯甲醚［J］. 精细化工，2021，38（8）：1590-1596.［10］ Yan Q H，Nie Y，Yang R Y，et al. Highly dispersed CuyAlOx mixed oxides as superior low-temperature alkali metal and SO2 resistant NH3-SCR catalysts［J］. Applied Catalysis A（General） ，2017（538）：37-50.［11］ Kumar P A，Reddy M P，Ju L K，et al. Low temperature propylene SCR of NO by copper alumina catalyst［J］. Journal of Molecular Catalysis A（Chemical），2008，291（1/2）：66-74.［12］ Zhang Y S，Li C M，Yu C，et al. Synthesis，characterization and activity evaluation of Cu-based catalysts derived from layered double hydroxides （LDHs） for de-NOx reaction［J］. Chemical Engineering Journal，2017（330）：1082-1090.［13］ Nie Y，Yan Q H，Chen S N，et al. CuTi LDH derived NH3-SCR catalysts with highly dispersed CuO active phase and improved SO2 resistance［J］. Catalysis Communications，2017（97）：47-50.［14］ Yuan D L，Li X Y，Zhao Q D，et al. Effect of surface Lewis acidity on selective catalytic reduction of NO by C3H6 over calcined hydrotalcite［J］. Applied Catalysis A（General），2013（451）：176-183.［15］ Yan Q H，Gao Y S，Li Y R，et al. Promotional effect of Ce doping in Cu4Al1Ox–LDO catalyst for low-T practical NH3-SCR： Steady-state and transient kinetics studies［J］. Applied Catalysis B（Environmental），2019（255）：117749.［16］ Yan Q H，Chen S N，Zhang C，et al. Synthesis and catalytic performance of Cu1Mn0.5Ti0.5Ox mixed oxide as low-temperature NH3-SCR catalyst with enhanced SO2 resistance［J］. Applied Catalysis B（Environmental），2018（238）：236-247.［17］ Yan Q H，Chen S N，Qiu L，et al. Synthesis of CuyMnzAl1-zOx mixed oxide as low-temperature NH3-SCR catalyst with enhanced catalytic performance［J］. Dalton Transactions，2018，47（9）：2992-3004.［18］ Yan Q H，Chen S N，Zhang C，et al. Synthesis of Cu0.5Mg1.5Mn0.5Al0.5Ox mixed oxide from layered double hydroxide precursor as highly efficient catalyst for low-temperature selective catalytic reduction of NOx with NH3［J］. Journal of Colloid & Interface Science，2018（526）：63-74.［19］ 刘江宁. 强抗硫CuAl基复合氧化物脱硝催化剂的构筑及其性能提升机制研究［D］. 太原：太原理工大学，2021.［20］ Wu X，Meng H，Du Y L，et al. Fabrication of highly dispersed Cu-based oxides as desirable NH3-SCR catalysts via employing CNTs to decorate the CuAl-Layered double hydroxides［J］. ACS Applied Materials & Interfaces，2019，11（36）：32917-32927.［21］ Meng H，Liu J N，Du Y L，et al. Novel Cu-based oxides catalyst from one-step carbothermal reduction decomposition method for selective catalytic reduction of NO with NH3［J］. Catalysis Communications，2019（119）：101-105.［22］ 刘雪贞. 钛/碳（CNTs）载铜铝类水滑石衍生复合氧化物低温NH3-SCR性能研究［D］. 太原：太原理工大学，2020.［23］ Hou B H，Du Y L，Liu X Z，et al. Tunable preparation of highly dispersed NixMn-LDO catalysts derived from NixMn-LDHs precursors and application in low-temperature NH3-SCR reactions［J］. RSC Advances，2019，9（42）：24377-24385.［24］ Du Y L，Liu J N，Li X J，et al. SCR performance enhancement of NiMnTi mixed oxides catalysts by regulating assembling methods of LDHs based precursor［J］. Applied Organometallic Chemistry，2020，34（4）：5510.［25］ 杨宝拴，次超，王若男，等. Ni（Mn, Cu）Ti-LDHs衍生催化剂低温NH3-SCR性能研究［J］. 天然气化工（C 1化学与化工），2020，45（2）：11-16.［26］ Zhang X Y，Yan Q H，Wang Q. Design of practical Ce/CoMnAl-LDO catalyst for low-temperature NH3-SCR［J］. Catalysis Communications，2020（142）：106037.［27］ 刘倍宏. 活性炭负载铜锰基催化剂的制备及其对焦炉烟气中NOx和CO协同控制研究［D］. 北京：北京林业大学，2020.［28］ Chen S N，Yan Q H，Zhang C，et al. A novel highly active and sulfur resistant catalyst from Mn-Fe-Al layered double hydroxide for low temperature NH3-SCR［J］. Catalysis Today，2019（327）：81-89.［29］ Chen S N，Vasiliades M A，Yan Q H，et al. Remarkable N2-selectivity enhancement of practical NH3-SCR over Co0.5Mn1Fe0.25Al0.75Ox-LDO： The role of Co investigated by transient kinetic and DFT mechanistic studies［J］. Applied Catalysis B（Environmental），2020，277（2）：119186.［30］ Wu X，Wang R N，Du Y L，et al. Performance enhancement of NH3-SCR via employing hydrotalcite-like precursor to induce the decoration of NiO by TiO2 phase［J］. Molecular Catalysis，2019（467）：150-160.

备注/Memo

备注/Memo:

中国石油天然气集团有限公司基金资助项目（项目编号：2020 D-2315）

常用功能

更新日期/Last Update: 2023-11-10