Structure and properties of metallocene polyethylene of raised temperature resistance pipe resin
作者:
朱珍珍1; 张鹏1; 李丽1; 朱裕国2 a; 金琳2 b
1.中国石油石油化工研究院 兰州化工研究中心， 甘肃 兰州 730060；2.中国石油兰州石化公司 a.规划发展处，b.石油化工厂，甘肃 兰州 730060
Author(s):
ZHU Zhen-zhen1;  ZHANG Peng1;  LI Li1;  ZHU Yu-guo2 a;  JIN Lin2 b
1.Lanzhou Petrochemical Research Center， Petrochemical Research Institute，PetroChina， Lanzhou 730060， China； 2. a. Planning and Development Department，b. Petrochemical Plant， Lanzhou Petrochemical Company，PetroChina， Lanzhou 730060， China
关键词:
茂金属; 管材料; 聚乙烯; 热性能; 相对分子质量及其分布; 流变性能
Keywords:
metallocene;  pipe resin;  polyethylene;  thermal property;  relative molecular mass and its distribution;  rheological property
分类号:
TQ 325.1+2
DOI:
DOI：10.19909/j.cnki.ISSN1009-0045.2022.02.0086
文献标识码:
B
摘要:
对3种茂金属耐热聚乙烯（PE-RT）管材料（ M 1，M 2和M 3）的基本物性、热性能、相对分子质量及其分布、力学性能、流变性能等进行分析表征，考察了3种PE-RT管材料的性能差异。结果表明： 3种PE-RT管材料均属于中密度聚乙烯产品，熔体流动速率相近；3种PE-RT管材料中，国产料M 1，M 2的分子质量分布较宽，熔点较低，结晶度小，韧性较好；进口料M 3的熔体拉伸强度较大，可拉伸性最佳，弯曲弹性模量高，具有良好的刚性。
Abstract:
The basic physical properties， thermal properties， relative molecular mass and its distribution， mechanical properties and rheological properties of three metallocene polyethylene of raised temperature resistant （PE-RT） pipe resin （M 1， M 2 and M 3） were investigated. Analysis and characterization was conducted to investigate the performance differences of the three PE-RT pipe resin. The results showed that the three PE-RT pipe resin were all medium density polyethylene products with similar melt flow rates； among the three PE-RT pipe resin， the domestic resin M 1 and M 2 had wider molecular mass distribution and lower melting point， smaller crystallinity， and better toughness， the imported resin M 3 had higher melt tensile strength， the best stretch ability， high flexural modulus and good rigidity.

参考文献/References

［1］ 王立娟， 何书艳， 门亚男， 等. 一种高密度PE-RTⅡ型管材树脂分子链结构剖析［J］. 中国塑料， 2016， 30（2）: 24-27.
［2］ 王群涛， 唐岩， 郭锐， 等. 结晶分级技术在耐热聚乙烯管材料研究中的应用［J］. 合成树脂及塑料， 2014， 31（2）: 13-16.
［3］ 田小青. 关于PE管材在给排水系统实际应用的情况分析［J］. 中国科技信息， 2011（10）: 290.
［4］ 李东华， 王群涛， 郭锐，等. 茂金属耐热PE-RT管材料的开发与生产［J］. 齐鲁石油化工， 2019， 47（1）: 5-8.
［5］ 李瑞， 姜艳峰， 吴双， 等. 双向拉伸聚乙烯的微观结构及热学表征［J］ .合成树脂及塑料， 2020， 37（2）: 63-66.

备注/Memo

备注/Memo:
-
更新日期/Last Update: 2022-03-10