Title:

Influence of vanadium and nickel contamination on performance of additives for increasing propylene production in fluid catalytic cracking

文章编号:

1009-0045（2022）06-0372-05

作者:

吕鹏刚; 刘涛; 潘志爽; 郑云锋; 黄校亮; 蔡进军; 王漫云; 段宏昌

中国石油石油化工研究院 兰州化工研究中心，甘肃 兰州 730060

Author(s):

L■ Peng-gang;  LIU Tao;  PAN Zhi-shuang;  ZHENG Yun-feng;  HUANG Xiao-liang;  CAI Jin-jun;  WANG Man-yun;  DUAN Hong-chang

Lanzhou Petrochemical Research Center， Petrochemical Research Institute， PetroChina， Lanzhou 730060， China

关键词:

流化催化裂化; 增产丙烯助剂; 抗重金属污染; 钒; 镍; 性能; 影响

Keywords:

fluid catalytic cracking; additives for increasing propylene production;  anti-heavy metal contamination;  vanadium;  nickel;  performance;  influence

分类号:

TE 621

DOI:

DOI：10.19909/j.cnki.ISSN1009-0045.2022.06.0372

文献标识码:

B

摘要:

采用浸渍法对流化催化裂化（FCC）中的增产丙烯助剂（LHP-A）进行了重金属钒、镍污染复配。考察了不同含量钒、镍单独或共同污染作用下对LHP-A的比表面积、相对结晶度和微反活性的影响，并分别在固定床微型反应评价装置（MAT）和先进的催化裂化评价装置（ACE）上评价了增产丙烯助剂相应污染复配后催化剂的反应性能。结果表明：无论LHP-A是否被重金属钒、镍单独或共同污染，只要FCC主催化剂复配了含质量分数10%的丙烯助剂后，丙烯收率均可提升4个百分点以上；在钒污染质量分数低于1%时，LHP-A具有良好的水热稳定性；当重金属镍污染LHP-A时，干气产率显著增加，但在钒污染量相同的前提下，镍的存在可以减缓钒对丙烯助剂性能的影响。

Abstract:

The heavy metal vanadium and nickel contamination were compounded by the impregnation method on LHP-A， an additive for increasing propylene production in fluid catalytic cracking（FCC）. Then， the influence of different contents of vanadium and nickel on the specific surface area， relative crystallinity and micro-reactivity of LHP-A under the contamination condition of different contents of vanadium and nickel alone or together were studied， and the reaction performance of the catalyst was evaluated in the fixed bed micro reaction evaluation unit（MAT） and the advanced catalytic cracking evaluation unit（ACE） after the corresponding contamination of the additive for increasing propylene production. The results showed that： no matter whether LHP-A was contaminated by vanadium and nickel alone or together， the yield of propylene would increase by more than 4 percentage points， as long as the FCC main catalyst was combined with 10% propylene additive. When the mass fraction of vanadium contamination was less than 1%， LHP-A had good hydrothermal stability. When LHP-A was contaminated by the heavy metal nickel， the dry gas yield increased significantly， but under the premise of the same amount of vanadium contamination， the presence of nickel was able to slow down the influence of vanadium on the performance of propylene additives.

参考文献/References

［1］ 张亮.稀土对催化裂化催化剂的影响及抗镍钒作用的研究［D］.兰州：兰州交通大学，2013.［2］ Gusev A A， Psarras A C， Triantafyllidis K S， et al. ZSM-5 additive deactivation with nickel and vanadium metals in the fluid catalytic cracking （FCC） process［J］. Ind Eng Chem Res， 2019， 59（6）， 2631-2641.［3］ 杜晓辉，任世宏，刘璞生，等.稀土对催化裂化催化剂抗钒污染性能的影响［J］.石油学报（石油加工），2020，36（4）：696-701.［4］ 李雪礼，谭争国，曹庚振，等.稀土基催化裂化抗钒助剂的研究与应用［J］.石化技术与应用，2015，33（1）：26-29.［5］ Pinto F V， Escobar A S， Oliveira B， et al. The effect of alumina on FCC catalyst in the presence of nickel and vanadium［J］. Appl Cata A（Gen）， 2010， 388（1/2）：15-21.［6］ 武俊平.催化裂化增产丙烯助剂LTB-1的工业应用［J］. 石油炼制与化工， 2007，38（5）：10-13.［7］ 吕鹏刚，刘涛，叶行，等.FCC工艺中提升增产丙烯助剂性能研究进展［J］.化工进展，2022，41（1）：210-220.［8］ 王国峰，吕延曾，赵洪军.钒对催化裂化催化剂的影响及其对策［J］.石化技术与应用，2012，30（4）：355-358.［9］ 黄蕾，张莉，高雄厚，等.催化裂化催化剂抗重金属技术应用与进展［J］.工业催化，2018，26（6）：1-7.［10］ Santos L， Grisolia R G， Pimenta R D， et al. Cyclohexane as a probe to nickel vanadium interaction in FCC catalysts［J］. Studies in Surface Science & Catalysis， 2001， 139（1）：343-350. ［11］ Etim U J， Xu B， Bai P， et al. Role of nickel on vanadium poisoned FCC catalyst： A study of physiochemical properties［J］.Journal of Energy Chemistry， 2016， 25（4）： 667-676.